MEGAFIL 235 M is a metal-cored seamless wire that deposits a 0.5% Mo type weld metal. It is primarily intended for similar composition steels, used where creep rupture strength and ductility operating at service temperatures up to 500°C are required. Wire suitable also for ordinary C-Mn steels when higher tensile strength is required. Diffusible hydrogen levels will be less than 4ml/100g of deposited weld metal, giving it more resistance to cracking. Applications: vessels (Mo steels up to 500°C), chemical plant, automatic and mechanized welding, steel structures, single and multi-pass welding, general fabrication, etc.
| AWS Classification | AWS A5.28: E80C-G H4 |
| Welding Position |  |
| Standard diameters: | 1.2 mm |
| Polarity | Direct Current Electrode Positive (DCEP) |
MEGAFIL 235 M is a metal-cored seamless wire that deposits a 0.5% Mo type weld metal. It is primarily intended for similar composition steels, used where creep rupture strength and ductility operating at service temperatures up to 500°C are required. Wire suitable also for ordinary C-Mn steels when higher tensile strength is required. Diffusible hydrogen levels will be less than 4ml/100g of deposited weld metal, giving it more resistance to cracking. Applications: vessels (Mo steels up to 500°C), chemical plant, automatic and mechanized welding, steel structures, single and multi-pass welding, general fabrication, etc.
| AWS Classification | AWS A5.28: E80C-G H4 |
| Welding Position | |
| Standard diameters: | 1.2 mm |
| Polarity | Direct Current Electrode Positive (DCEP) |
MEGAFIL 235 M is a metal-cored seamless wire that deposits a 0.5% Mo type weld metal. It is primarily intended for similar composition steels, used where creep rupture strength and ductility operating at service temperatures up to 500°C are required. Wire suitable also for ordinary C-Mn steels when higher tensile strength is required. Diffusible hydrogen levels will be less than 4ml/100g of deposited weld metal, giving it more resistance to cracking. Applications: vessels (Mo steels up to 500°C), chemical plant, automatic and mechanized welding, steel structures, single and multi-pass welding, general fabrication, etc.